Pengaruh Partikel Nanosilika Terhadap Sifat Tolak Air Bahan Isolasi Bionanokomposit

Aulia Aulia, Roan Alfajri, Eka Putra Waldi, Novizon Novizon

Abstract


The nature of hydropobicity plays an important role of an insulator, especially the outdoor insolator which is always exposed to hot, cold, humid weather and rain water. In the long run, the surface of the insulator can be damaged and its hydropobicity properties will be reduced or even lost so that surface discharge events will be easier to occur, especially in the rainy season. As a new material being developed, bionanocomposite insulation materials from LDPE, natural rubber and nanosilica fillers have passed several dielectric properties such as partial discharge characteristics under normal conditions and at higher temperature conditions. To complete the assessment of dielectric properties, a new bionanocomposite material hydropobicity was tested. There were 4 types of samples tested with the weight of the nanosilica material 1.5%, 3.0%, 4.5% and 6% of the total weight of the biocomposite sample. The test was carried out using a high-resolution camera to take pictures of the surface of the insulator sample that was dripped with water. The results show that nanosilica can increase the angle of contact of water with the bionanocomposite surface. This increase indicates an increase in the hydropobicity of bionanocomposite material

Keywords : LDPE, Karet Alam, Natural Rubber, nanosilica, hydrophobisity

 

Abstrak

Sifat hidropobisitas memainkan peran penting dari sebuah isolator, terutama isolator pasang luar yang selalu terpapar oleh perubahan cuaca panas, dingin, lembab dan air hujan. Dalam jangka panjang, permukaan isolator bisa rusak dan sifat hidropobisitasnya akan berkurang bahkan hilang sehingga peristiwa peluahan permukaan akan lebih mudah terjadi, terutama pada musim hujan. Sebagai material baru yang sedang dikembangkan, bahan isolasi bionanokomposit dari polietilena berkerapatan rendah (LDPE), karet alam (NR) dan pengisi nanosilika telah melewati beberapa pengujian sifat dielektrik seperti karakteristik peluahan sebagian pada kondisi normal dan pada kondisi suhu yang lebih tinggi. Untuk melengkapi pengkajian sifat dielektrik, maka dilakukan pengujian sifat hidropobisitas bahan bionanokomposit yang baru tersebut. Sampel yang diuji ada 4 jenis dengan kada berat bahan nanosilika 1,5%, 3,0%, 4,5% dan 6% dari berat total sampel biokomposit. Pengujian dilakukan dengan menggunakan kamera beresolusi tinggi untuk mengambil gambar permukaan sampel isolator yang ditetesi air. Hasil menunjukan bahwa nanosilika dapat memperbesar sudut kontak air dengan permukaan bionanokomposit. Peningkatan ini mengindikasikan meningkatnya sifat hidropobisitas material bionanokomposit.

Kata Kunci : Biokomposit, Hidropobisitas, Karet Alam, LDPE


Full Text:

PDF

References


Yang, D., et al., Enhanced electromechanical properties of natural rubber using highly efficient and cost-effective mussel-inspired modification of TiO2 nanoparticles. Applied Surface Science, 2019: p. 143638.

Vélez, J.S., S. Velásquez, and D. Giraldo, Mechanical and rheometric properties of gilsonite/carbon black/natural rubber compounds cured using conventional and efficient vulcanization systems. Polymer Testing, 2016. 56: p. 1-9.

Arief, Y.Z., et al. Effects of nanosilica and nanotitania on partial discharge characteristics of natural rubber-lldpe blends as high voltage insulation material. in Electrical Insulating Materials (ISEIM), Proceedings of 2014, International Symposium on. 2014.

Makmud, M.Z.H., et al., Ageing and Degradation Mechanism of Linear Low Density Polyethylene-Natural Rubber Composites due to Partial Discharge. 2012 Ieee International Conference on Power and Energy (Pecon), 2012: p.985-989.

Aji Suryo Alam*), A.S., and Agung Nugroho, Analisa Pengaruh Variasi dan Komposisi Bahan Pengisi Terhadap Unjuk Kerja Sampel Isolator Resin Epoksi Silane. 2013. VOL.2, NO. 3.

Moh Toni Prasetyo1*, A.S., Efektifitas Pemanfaatan Pasir Pantai Berkalsium Sebagai Material Pengisi Bahan Isolasi Resin Epoksi Untuk Isolator Listrik.

Anhar Ashari, A.S., and Bambang Winardi, Analisa Pengaruh Kontaminan Pantai Terhadap Unjuk Kerja Sampel Isolator Bahan Keramik Sebelum dan Sesudah Dilapisi Minyak Silikon. 2012

Basanta Kumar Gautam, T.Y., Kazuma Yamada, Shuhei Matsushita, Kenji Sakanishi and Ryosuke Matsuoka, Effect of Non-soluble Contaminants on The Flashover Voltages of Hydrophobic Polymer Insulators. 2006

M.Putra Nurjanah, F., Analisis Pengaruh Endapan Polutan dengan Metode Equivalent Salt Deposit Density (ESDD) terhadap Tegangan Korona pada Isolator Pin Post di Jaringan Distribusi 20 kV Pekanbaru.JOMTeknik, 2016. vol.3.

Syakur, A., et al., Analisis Sifat Hidrofobik Permukaan Hdpe Berdasarkan Nilai Total Harmonic Distortion. TELKOMNIKA (Telecommunication Computing Electronics and Control), 2009. 7(2): p. 109.

Shirazi, M.M.S., H. Borsi, and E. Gockenbach. Effect of TiO2 nanofillers on electrical, thermal and mechanical parameters of epoxy resin. in 2012 IEEE International Symposium on Electrical Insulation. 2012.

Setiawan, M.H., Reparasi Sampel dan Pengujian Tensile Strength Isolasi Nanokomposit di Pusat Teknologi Material (PTM – BPPT). 2018.




DOI: https://doi.org/10.25077/jnte.v9n2.716.2020

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution 3.0 License.

  

        

 

.
 Statistic and Traffic